Ferro Frit 9146
Dense zircon white frit leadless frit
Alternate Names: Frit DA9146
A frit is a type of ceramic glass. It is a combination of materials which are melted together to render them insoluble and resistant to acid attack. They are therefore a means of introducing certain materials into a glaze which would otherwise be toxic. Frits can be used alone as low-temperature glazes e.g. Raku and Majolica, but generally, they form the basis of a glaze recipe.
LEAD FRITS Glazes based on lead frits produce a shiny, durable finish and give brightness and clarity of colour when used in conjunction with oxides, stains, slips etc. While they can be used on all earthenware clays, they are particularly suited for red clay.
Oxide Analysis Formula
CaO 6.00% 0.461
MgO 0.60% 0.064
Na2O 6.00% 0.417
ZnO 1.10% 0.058
Al2O3 4.10% 0.173
B2O3 13.53% 0.837
SiO2 56.45% 4.046
ZrO2 12.23% 0.428
Oxide Weight 430.84
Formula Weight 430.84
If this formula is not be unified correctly please contact us.
GSPT - Frit Softening Point 573C
MLRG - Frit Melting Range (C) 1040-1100C
GTTM - Glass Transition Temperature 628 C Top of Form
Dense zircon white frit leadless frit
Alternate Names: Frit DA9146
A frit is a type of ceramic glass. It is a combination of materials which are melted together to render them insoluble and resistant to acid attack. They are therefore a means of introducing certain materials into a glaze which would otherwise be toxic. Frits can be used alone as low-temperature glazes e.g. Raku and Majolica, but generally, they form the basis of a glaze recipe.
LEAD FRITS Glazes based on lead frits produce a shiny, durable finish and give brightness and clarity of colour when used in conjunction with oxides, stains, slips etc. While they can be used on all earthenware clays, they are particularly suited for red clay.
Oxide Analysis Formula
CaO 6.00% 0.461
MgO 0.60% 0.064
Na2O 6.00% 0.417
ZnO 1.10% 0.058
Al2O3 4.10% 0.173
B2O3 13.53% 0.837
SiO2 56.45% 4.046
ZrO2 12.23% 0.428
Oxide Weight 430.84
Formula Weight 430.84
If this formula is not be unified correctly please contact us.
GSPT - Frit Softening Point 573C
MLRG - Frit Melting Range (C) 1040-1100C
GTTM - Glass Transition Temperature 628 C Top of Form